| BIOPLAST GF 106/02 is BIOTEC's trademark for a completely new, plasticizer-free thermoplastic material. As a result of plasticizer absence no material built-up or steam occurs during processing of BIOPLAST GF 106/02. The material is extremely suitable for blown film extrusion, sheet film extrusion, tube extrusion and injection moulding of completely biodegradable products. The complete biodegradability and other functional properties enable the converter to advance in production areas, which could not be reached with traditional thermoplastic materials. The potato starch used for BIOPLAST GF 106/02 is native and not blended with plasticizer (which would be necessary for example to produce thermoplastic starch, TPS). BIOPLAST GF 106/02 therefore exhibits outstanding processing and performance characteristics as well as an excellent shelf life. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 to 1.30 | g/cm³ | ISO 1183 |
| Apparent Density | 0.74 to 0.80 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 2.5 to 3.5 | g/10 min | ISO 1133 |
| Particle Size | 1.50 to 2.50 | mm | |
| Water Content | < 0.50 | wt% | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability (80.0 µm) | 750 | cm³/m²/bar/24 hr | DIN 53380-3 |
| Film Thickness - Tested | > 10 | µm | ISO 2286-3 |
| Tensile Strength | ISO 527-3 | ||
| MD : 23°C, 10 µm | 20.0 to 35.0 | MPa | |
| TD : 23°C, 10 µm | 20.0 to 35.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 10 µm | 600 to 900 | % | |
| TD : Break, 10 µm | 600 to 900 | % | |
| Water Vapor Transmission Rate (80 µm) | 120 | g/m²/24 hr | DIN 53122 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.10 to 1.20 | g/cm³ | ISO 1133 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1486 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sylvin 6227-83 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Karina BLUE COLOR CONCENTRATE 06/152-FC-LMP (SDB) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND 750D10/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NILAMID® XS3 CF30 TF15 | Nilit Plastics | Nylon, Unspecified | NILAMID® |