DOWLEX™ 2098P
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0vMamY_DOWLEX-2098P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DOWLEX 2098P Polyethylene Resin is a formulated linear low density resin offering excellent tear strength, medium stiffness, outstanding toughness and puncture resistance for films used in food contact applications. When used unmodified and processed according to good manufacturing practices, this resin is technically suitable for food contact end use. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 12.8 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 15.2 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 39.6 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 34.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 670 | % | ASTM D882 |
| TD : Fracture, 38 µm | 780 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 220 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 240 | g | ASTM D1922 |
| TD : 38 µm | 730 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm) | 45 | ASTM D2457 | |
| Haze (38.1 µm) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 221 - 243 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 熔体温度：430-470°F (220-240°C) 放大比：2:1 厚度：0.5-3.0 密尔 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Techsil PU 2600FS/WT | Techsil Limited | PUR, Unspecified | Techsil |
| Taizhou Phenolic PF2A1-131 | Taizhou Changxiong Plastic Co., Ltd. | Phenolic | Taizhou Phenolic |
| WPP PP PPC4TF1.3-Natural | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| KOPLA PC KBP1000 | KOPLA Co., Ltd. | PBT | KOPLA PC |
| PENTAMID AHT GV30 H1 ungefärbt | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |