Braskem PE GM5010T2U
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0twgtP_Braskem-PE-GM5010T2U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GM5010T2U is a High Density Polyethylene compound with high molar mass specially developed for the manufacturing of jacketing of umbilicals. It is produced with bimodal technology, shows high mechanical properties and has excellent resistance to stress cracking. GM5010T2U contains carbon black pigment that protects it against ultraviolet radiation action and photodegradation. Application: Jacketing of umbilicals, risers and flowlines for oil field platforms. Process: Extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.955 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.45 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (2.00 mm, 100% Igepal, Compression Molded, F50) | > 1000 | hr | ASTM D1693 |
| Carbon Black Content | 2.3 to 2.7 | % | ASTM D1603 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 23.0 | MPa | |
| Break, Compression Molded | 34.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, Compression Molded | 9.1 | % | |
| Break, Compression Molded | 800 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 1090 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 220 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 70.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 1 |
| Oxidation Induction Time (220°C) | > 50 | min |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 3 Series 385A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| XANTAR® MX 1004 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Hapflex™ 564 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| Loyblend® TY-1000 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+PBT | Loyblend® |
| Durethan® AKV 30 HR H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |