ISPLEN® PM 470 XT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0rnSIO_ISPLEN-PM-470-XT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer, 40% mineral fillers reinforced and medium melt flow rate. ISPLEN® PM470 XT shows a high stiffness, as well as a low warpage and shrinkage behaviour. The product is high heat and chemical stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 1.0 to 1.1 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 22.0 | MPa | |
| Break | 17.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 2.5 | % | |
| Break | 37 | % | |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 1.0 | kJ/m² | |
| -20°C | 1.2 | kJ/m² | |
| 0°C | 1.3 | kJ/m² | |
| 23°C | 1.6 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 12 | kJ/m² | |
| -20°C | 13 | kJ/m² | |
| 0°C | 16 | kJ/m² | |
| 23°C | 38 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 83.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 57.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A120 |
| -- | 97.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC EVA VA920 | Lotte Chemical Corporation | EVA | SEETEC EVA |
| MOSTEN GB 218 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Avantra® 8030 | PMC Group Polymer Products | PS (HIPS) | Avantra® |
| Karina WHITE PVC COMPOUND 650-10/1 (MP-1.0) (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 880-35/ 1-F-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |