EVERCAP™ DMDA-1206 NT 7
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | EVERCAP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0rTYA8_EVERCAPDMDA1206NT7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EVERCAP™ DMDA-1206 NT 7 High Density Polyethylene (HDPE) Resin from Dow enables the right performance properties to meet demanding closure and fitment application needs. It is intended for use in injection molding applications such as caps and closures and other injection molding applications. This resin has been designed to meet demanding performance requirements such as environmental stress crack resistance, excellent sensory, stiffness, impact strength, while offering excellent processing characteristics. Targeted Applications and Product Characteristics:
Consult the regulations for complete details. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.8 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 12.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.9 | MPa | ASTM D638 |
| Fracture | 22.8 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 1100 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1070 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 84.1 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 72.8 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 128 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 131 | °C | Internal method |
| Additional Information |
|---|
| Plaque molded and tested in accordance with ASTM D4976. |
| Note Message | |
|---|---|
| 1 . | Type S |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REBOUND® 25 | Smooth-On, Inc | Silicone | REBOUND® |
| ADMER™ QF541E | Mitsui Chemicals Europe GmbH | PP Copolymer | ADMER™ |
| Ebalta GM 978 / D | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| EPO-TEK® 310M-1 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| 3M™ Dyneon™ PTFE Compound 310999212 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |