Nypel® 6030G HS BK
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Nypel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0r2W9D_Nypel-6030G-HS-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Nypel 6030G HS BK is a 30% glass fiber reinforced, heat stabilized, black injection molding PA6 compound. Applications Nypel 6030G HS BK is generally recommended for applications such as bolts, racks, automotive underhood components, pressure regulator housings, caps and general industrial applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.1 | % | |
| Saturation, 23°C | 6.7 | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| -40°C | 8740 | MPa | |
| 23°C | 9580 | MPa | |
| 80°C | 3820 | MPa | |
| 121°C | 2730 | MPa | |
| Tensile Stress | ISO 527-2 | ||
| Break, -40°C | 220 | MPa | |
| Break, 23°C | 155 | MPa | |
| Break, 80°C | 80.0 | MPa | |
| Break, 121°C | 65.0 | MPa | |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8070 | MPa | ISO 178 |
| Flexural Stress (23°C) | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.6 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 54 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 6.5 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 219 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| CLTE | |||
| Flow | 2.5E-5 | cm/cm/°C | |
| Transverse | 6.7E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 0.810 mm | 130 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C | |
| RTI Imp | UL 746 | ||
| 0.810 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 120 | °C | |
| RTI Str | UL 746 | ||
| 0.810 mm | 130 | °C | |
| 1.50 mm | 140 | °C | |
| 3.00 mm | 140 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.810 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| METALCAP PPC371B73 | Polyram Ram-On Industries | PP Copolymer | METALCAP |
| TITANZEX® HM5001 | Lotte Chemical Titan (M) Sdn. Bhd. | HDPE | TITANZEX® |
| VINIKA® CB95GA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| APEX® RE 8118 | Teknor Apex Company | PVC, Rigid | APEX® |
| Kuraray Poval® PVA 117S | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |