Lucofin® 7440 HFFR
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Lucobit AG |
| Trademark: | Lucofin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0r0y10_Lucofin-7440-HFFR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product description Lucofin® 7440 HFFR is a thermoplastic, halogen free flame retardant and low smoke compound for the insulation and/or sheating of cables. Lucofin® 7440 HFFR combines good extrusion properties with flame retardancy. The properties of Lucofin® 7440 HFFR are in compliance with VDE 0207 part 24(HM 2/4), VDE 0207 part 23 (HJ2), BS 6724 as well as other power and telecom standards. Applications and markets Target markets include -among others- power and telecom cables as well as construction and optical fiber cables. Lucofin® 7440 HFFR is designed in order to avoid both smoke and corrosive gases in case of a fire. Cables in trains, ships, tunnels, office buildings, public houses and off-shore installations are only some examples. Due to its low water absorption, excellent low temperature properties and good ageing resistance Lucofin® 7440 HFFR is specifically suited for the following applications: Cables in wet areas
Cables in cold areas
Cables in hot areas
Packaging Granules in 25 kg bags |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 6.5 | g/10 min | ISO 1133 |
| Water Absorption 1(70°C) | 0.500 | mg/cm² | IEC 60811-1-3 |
| pH | 6.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elongation at break- variation from original 2(70°C) | -3.0 | % | |
| Tensile strength- variation from original 3(70°C) | -11 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile strength retention rate | 94 | % | BS 6724 |
| Elongation retention rate- at break | 97 | % | BS 6724 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold Elongation | 120 | % | IEC 60811-1-4 |
| Hot pressing test 4(90°C) | 10 | % | IEC 60811-3-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | 3.20 | µS/cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | mg/g | IEC 754-1 | |
| Toxicity | 2.80 | EN 50305 |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 140°C) | 40 | MU | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 52 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 60811-1-1 | ||
| -- | 11.5 | MPa | IEC 60811-1-1 |
| 110°C 5 | 10.8 | MPa | IEC 60811-1-1 |
| Tensile Strain | IEC 60811-1-1 | ||
| Fracture | 190 | % | IEC 60811-1-1 |
| Fracture, 110°C 6 | 160 | % | IEC 60811-1-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | ||
| -- 7 | 1.7E+14 | ohms | IEC 60093 |
| -- 8 | 4.1E+14 | ohms | IEC 60093 |
| Volume Resistivity | IEC 60093 | ||
| -- 9 | 6.9E+14 | ohms·cm | IEC 60093 |
| 70°C 10 | 2.1E+14 | ohms·cm | IEC 60093 |
| Dielectric Constant | IEC 60250 | ||
| 50 Hz 11 | 3.60 | IEC 60250 | |
| 20°C, 50 Hz 12 | 5.30 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz 13 | 7.4E-3 | IEC 60250 | |
| 20°C, 50 Hz 14 | 0.064 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 38 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 165 | °C | |
| Cylinder Zone 4 Temp. | 175 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Melt Temperature | 200 - 220 | °C | |
| Die Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | 10 days |
| 2 . | Oil Ageing IRM 902, 4 h |
| 3 . | Oil Ageing IRM 902, 4 h |
| 4 . | 4 hours |
| 5 . | Aged 7 days |
| 6 . | Aged 7 days |
| 7 . | 70°C, 7 days duration of water immersion |
| 8 . | 0 h duration of water immersion |
| 9 . | 0 h duration of water immersion |
| 10 . | 7 days duration of water immersion |
| 11 . | 0 h duration of water immersion |
| 12 . | 24 h duration of water immersion |
| 13 . | 0 h duration of water immersion |
| 14 . | 24 h duration of water immersion |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 6080 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| AVALON® 95 AB | Huntsman Corporation | TPU-Polyester | AVALON® |
| DURANEX® 2002K | Polyplastics Co., Ltd. | PBT | DURANEX® |
| INEOS HDPE T50-200-178 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| LUVOCOM® 80-8222/EG | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |