Glastic UTS 141 is a fiberglass-reinforced laminate. This resin is ideal for applications requiring flame and heat resistance, as well as applications requiring higher retention of properties after heat aging. Glastic UTS 141 is ideal for a wide variety of applications, including intricate punchings for switches, switch plates, controls, control panels, and terminal boards. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (yield, 1.60mm) | 55.2 | MPa | ASTM D638 |
| Flexural Strength (1.60 mm) | 124 | MPa | ASTM D790 |
| Compressive Strength (1.60 mm) | 207 | MPa | ASTM D695 |
| Shear Strength | 96.5 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (1.60 mm) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow (1.60 mm) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.60 mm) | 130 | °C | UL 746 |
| RTI (1.60 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1(1.60 mm, in Air) | 12 | kV/mm | ASTM D149 |
| Arc Resistance (1.60 mm) | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| NEMA Grade: GPO-2/GPO-2PMilitary Specification: L-P 509/GPO-2Ignition Time: 75 minBurn Time: 85 min |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CP PRYME® Polypropylene PPH100-4M | Chase Plastics Services Inc. | PP Homopolymer | CP PRYME® Polypropylene |
| Durethan® T 7141 00000 | LANXESS GmbH | PBT+PET | Durethan® |
| Hostacom G2 N01 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Karina BLACK PVC COMPOUND 808D48/1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LG SAN 80HFICELLHK | LG Chem Ltd. | SAN | LG SAN |