NORYL™ PVX0800 resin
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0pL476_NORYL-PVX0800-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL PVX0800 resin is a high flow, V0 = 1.5 mm grade, suitable for a variety of electronics applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 260°C/5.0 kg | 22.0 | cm³/10min | |
| 280°C/5.0 kg | 47.0 | cm³/10min | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.070 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2670 | MPa | ASTM D638 |
| -- | 2580 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 53.0 | MPa | ISO 527-2/50 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 42.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 2.7 | % | ISO 527-2/50 |
| Break 5 | 15 | % | ASTM D638 |
| Break | 27 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2700 | MPa | ASTM D790 |
| 6.40 mm | 2700 | MPa | ASTM D790 |
| -- 7 | 2390 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 83.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 86.0 | MPa | ASTM D790 |
| Yield, 6.40 mm | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10(-30°C) | 6.0 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 100 | J/m | ASTM D256 |
| 23°C | 250 | J/m | ASTM D256 |
| -30°C 11 | 7.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 88.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 6.40 mm | 92.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 13 | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 78.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 79.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525 15 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (280°C, 1500 sec^-1) | 98.0 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 216 to 266 | °C | |
| Middle Temperature | 227 to 271 | °C | |
| Front Temperature | 238 to 277 | °C | |
| Nozzle Temperature | 249 to 277 | °C | |
| Processing (Melt) Temp | 249 to 277 | °C | |
| Mold Temperature | 54.4 to 76.7 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm | |
| Vent Depth | 0.038 to 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | 80*10*4 mm |
| 15 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 285A2R30023 Natural, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Mowiol® 4-88 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| NEXT REGRIND PBT 420-400RG | NEXT Specialty Resins, Inc. | PBT | NEXT REGRIND |
| Chemlon® 109-33 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| HiFill® PA6 GF/M15 A1 BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |