EVAL™ SP434A
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | EVAL Europe nv |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0nsvzV_EVAL-SP434A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EVAL™ SP434A is an Ethylene Vinyl Alcohol (EVOH) product. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.9 | g/10 min | |
| 210°C/2.16 kg | 11 | g/10 min | |
| 230°C/2.16 kg | 20 | g/10 min | |
| 250°C/2.16 kg | 28 | g/10 min | |
| Ethylene Content | 32.0 | mol% | Internal Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Transmission Rate | 0.078 | cm³·mm/m²/atm/24 hr | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Flexural Modulus | 4700 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability 1 | ISO 14663-2 | ||
| 20°C, 65% RH | 0.010 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.052 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 2 | 2.7 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -- | 2.0 | kJ/m² | |
| -40°C | 2.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 55.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 160 | °C | ISO 306 |
| Melting Temperature | 181 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 158 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Annex C |
| 2 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP6410 0003 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| Sylvin 5189-60D Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NEXUS Reprocessed Nylon 66 G33 RBK | Nexus Resin Group, LLC. | Nylon 66 | NEXUS Reprocessed |
| Generic PLA | Generic | PLA | Generic |
| Karina BLACK PVC COMPOUND -E 806D48/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |