SABIC® HDPE FI1157
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0k9ivL_SABIC-HDPE-FI1157.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE FI1157 is a high molecular high density polyethylene copolymer grade typically used for blown film applications. Its high molecular weight, broad molecular weight distribution and high density enables convertors to produce film with low gels level, high stiffness, impact resistance and with narrow gauge tolerances at low film thickness. SABIC® HDPE FI1157 can be processed at high throughput with good bubble stability. Typical applications SABIC® HDPE FI1157 is typically used for the production of inliners, bitumen release foils, lamination and paper lamination films, labels, artificial paper, thin films for bag on roll and heavy duty bags. Processing conditions Melt Temperature: 200-225°C Frost Line Height: 6-8 times die cross-cut BUR: 3-5 Film properties Film properties have been measured at 20 µm blown film with a BUR = 4. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.957 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 11 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.35 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ISO 868 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm | 50.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm | 45.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 20 µm | 400 | % | ISO 527-3 |
| TD : Break, 20 µm | 450 | % | ISO 527-3 |
| Dart Drop Impact 1(20 µm) | 240 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 75.0 | °C | ISO 306/B |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 6383-2 | ||
| MD : 20.0 µm | 200.0 | kN/m | ISO 6383-2 |
| TD : 20.0 µm | 450.0 | kN/m | ISO 6383-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 - 225 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimePart® PLUS PA 2221 | EOS GmbH | Nylon 12 | PrimePart® |
| PRL PC-BR1-(color)-5 | Polymer Resources Ltd. | PC | PRL |
| RJM SD101G30 | RJM International, Inc. | PC | RJM |
| Techsil RTV1084G | Techsil Limited | Silicone | Techsil |
| Viprene™ G45D-32U-BLK | Alliance Polymers & Services | TPV | Viprene™ |