TOTAL Polyethylene Lumicene® M 2711 PCE

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polyethylene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0haOl4_TOTAL-Polyethylene-Lumicene-M-2711-PCE.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Lumicene® mPE M2711 PCE is a Metallocene based Linear Low Density Polyethylene with hexene as comonomer. This product contains slip and anti-block agents. Lumicene® mPE M2711 PCE can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant down gauging potential. Lumicene® mPE M2711 PCE is especially dedicated to film applications requiring low coefficient of friction (COF) and blocking properties while maintaining good optics, particularly in blend and in coextrusion with LLDPE or LDPE. Lumicene® mPE M2711 PCE is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, deep freeze, collation shrink and lamination.

General Information
Additive	Processing aid Anti-caking agent Antioxidation slip agent
Features	Low density smoothness Optical hexene comonomer Anti-caking property Antioxidation
Uses	Packaging Films Laminate Bags Mixing
Processing Method	Blow film Co-extrusion molding

Physical	Nominal Value	Unit	Test Method
Density	0.927	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.90	g/10 min	ISO 1133

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	40	µm
Tensile Stress			ISO 527-3
MD : Yield, 40 µm	13.5	MPa	ISO 527-3
TD : Yield, 40 µm	14.0	MPa	ISO 527-3
MD : Break, 40 µm	48.0	MPa	ISO 527-3
TD : Break, 40 µm	51.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Break, 40 µm	650	%	ISO 527-3
TD : Break, 40 µm	720	%	ISO 527-3
Dart Drop Impact (40 µm)	230	g	ISO 7765-1
Elmendorf Tear Strength			ISO 6383-2
MD : 40 µm	60	N	ISO 6383-2
TD : 40 µm	170	N	ISO 6383-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	118	°C	ISO 306
Melting Temperature	119	°C	ISO 11357-3

Optical	Nominal Value	Unit	Test Method
Gloss (45°)	65		ASTM D2457
Haze	8.0	%	ISO 14782

Extrusion	Nominal Value	Unit
Melt Temperature	180 - 230	°C

Extrusion instructions
Lumicene® mPE M2711 PCE is typically extruded at a melt temperature around 200°C. Lumicene® mPE M2711 PCE can be blown easily at any of the following conditions:Temperature: 180 to 230°C, BUR: 1.5:1 to 4.5:1, Die gap: 0.8 to 2.8 mmFilm test figures obtained using laboratory test specimens produced with the following extrusion conditions 45 mm screw diameter, L/D = 30 die diameter = 20 mm, die gap = 1.4 mm, BUR = 2.5:1, temperature = 210°C

Extrusion instructions

Lumicene® mPE M2711 PCE is typically extruded at a melt temperature around 200°C. Lumicene® mPE M2711 PCE can be blown easily at any of the following conditions:Temperature: 180 to 230°C, BUR: 1.5:1 to 4.5:1, Die gap: 0.8 to 2.8 mmFilm test figures obtained using laboratory test specimens produced with the following extrusion conditions 45 mm screw diameter, L/D = 30 die diameter = 20 mm, die gap = 1.4 mm, BUR = 2.5:1, temperature = 210°C

Resin Grade	Manufacturer	Category	Trademark
RTP EMI 331 E FR	RTP Company	PC	RTP
SPESIN® KP513	Kolon Plastics, Inc.	PBT	SPESIN®
Sup-tech A801	Shanghai Suptech Engineering Plastics Co. Ltd.	Nylon 66	Sup-tech
LEXAN™ HPS2REU resin	SABIC Innovative Plastics Europe	PC	LEXAN™
Osterlene® HD0752	Osterman & Company	HDPE	Osterlene®