Bormod™ HD905CF
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Bormod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0hVugk_Bormod-HD905CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bormod HD905CF is a high cristallinity homopolymer film resin, based on special Borstar nucleating technology. This grade is suitable for the manufacturing of unoriented films on chill roll processes. For the cast film process it is recommended to use rather high chill roll temperatures in the range of 40-55°C to obtain the optimum film stiffness. Optical properties will not be deteriorated as with conventional homo or copolymers at these temperatures. Bormod HD905CF is recommended for:
Bormod HD905CF is optimised to deliver:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (Injection Molded) | 2250 | MPa | ISO 178 |
| Coefficient of Friction | 0.30 to 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Force 1(50 µm) | 500 | N | ISO 7765-2 |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, Cast Film | 2100 | MPa | |
| TD : 50 µm, Cast Film | 1900 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, Cast Film | 40.0 to 50.0 | MPa | |
| TD : 50 µm, Cast Film | 35.0 to 45.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 150 | % | |
| TD : Break, 50 µm, Cast Film | 10 | % | |
| Instrumented Dart Impact (50 µm, Cast Film, Total Energy) | 1.00 | J | ISO 7765-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 158 | °C | ISO 306/A |
| Melting Temperature (DSC) | 167 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.0 µm, Cast Film) | > 80 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | < 8.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L AB605 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| RTP 4285 TFE 5 | RTP Company | PI, TP | RTP |
| Versaflex™ FFC 2882-50 | PolyOne Corporation | TPE | Versaflex™ |
| Capilene® SG 50 | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| LUVOCOM® 50/TF/15/NAT | LEHVOSS Group | PC | LUVOCOM® |