FRblend® PP-1303
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0hCbH4_FRblend-PP-1303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PP-1303 is a high flow, flame retardant polypropylene compound. The flame retardant system is base on halogenated hydrocarbon compounds. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1330 | MPa | ASTM D638 |
| Tensile Strength | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 38 | % | ASTM D638 |
| Flexural Modulus | 1280 | MPa | ASTM D790 |
| Flexural Strength | 41.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 28 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 4.00 mm) | 109 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 190 to 200 | °C | |
| Nozzle Temperature | 200 to 210 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9700-90 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Ultramid® B35EG3 | BASF Corporation | Nylon 6 | Ultramid® |
| Bergamid™ A70 G30 WR NC103 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| CP PRYME® Nylon 6 N120L | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| Kuraray R-Polymer R-3109 | Kuraray Co., Ltd. | PVOH | Kuraray R-Polymer |