Generic PVDF
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0f7sGK_Generic-PVDF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PVDF This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.77 to 1.79 | g/cm³ | ASTM D792 |
| 23°C | 1.76 to 1.79 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 1.1 to 28 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 2.5 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.039 to 0.043 | % | ASTM D570 |
| 23°C, 24 hr | 0.039 to 0.040 | % | ISO 62 |
| Equilibrium, 23°C | 0.020 to 0.032 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 67 to 79 | ASTM D2240 | |
| 23°C | 68 to 78 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 477 to 2410 | MPa | ASTM D638 |
| 23°C | 2110 to 2520 | MPa | ISO 527-2 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 26.8 to 55.0 | MPa | |
| Break, 23°C | 22.0 to 45.0 | MPa | |
| Tensile Elongation | |||
| Yield, 23°C | 7.0 to 11 | % | ASTM D638 |
| Break, 23°C | 10 to 490 | % | ASTM D638 |
| Break, 23°C | 1.0 to 200 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 363 to 1860 | MPa | ASTM D790 |
| 23°C | 460 to 7250 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 27.4 to 68.4 | MPa | ASTM D790 |
| 23°C | 67.0 to 90.0 | MPa | ISO 178 |
| Compressive Strength (23°C) | 36.2 to 86.2 | MPa | ASTM D695 |
| Coefficient of Friction | 0.24 to 0.30 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 7.50 to 31.4 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 to 1000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 116 to 204 | °C | ASTM D794 |
| Glass Transition Temperature | -40.0 to -34.9 | °C | ASTM E1356 |
| Vicat Softening Temperature | 170 to 172 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 156 to 175 | °C | |
| -- | 142 to 175 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 127 to 141 | °C | ASTM D3418 |
| CLTE - Flow | |||
| -- | 1.2E-4 to 1.6E-4 | cm/cm/°C | ASTM D696 |
| -- | 1.3E-4 to 1.6E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1200 | J/kg/°C | ASTM C351 |
| Thermal Conductivity (23°C) | 0.17 to 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 to 1.1E+15 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 0.80 to 2.5E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 10 to 300 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 6.84 to 10.0 | ASTM D150 | |
| Dissipation Factor (23°C) | 0.010 to 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 42 to 45 | % | ASTM D2863 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | 520 to 3160 | Pa·s | ASTM D3835 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil FS-3600 | NuSil Technology | Silicone | NuSil |
| API PS 390 | American Polymers, Inc. | PS (GPPS) | API PS |
| Hanwha Total PP BJ51W | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Perfactory® ABS-tuff | EnvisionTEC, Inc. | Acrylic, Unspecified | Perfactory® |
| Sylvin 8940-80UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |