LNP THERMOCOMP MX92284 is a compound based on Polypropylene resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-M-92284 Product reorder name: MX92284 |
General Information | |
---|---|
Filler / Reinforcement |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus 1 | 4770 | MPa | ASTM D638 |
Tensile Strength (Break) | 49.6 | MPa | ASTM D638 |
Tensile Elongation (Break) | 3.1 | % | ASTM D638 |
Flexural Modulus | 3790 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C) | 91 | J/m | ASTM D256 |
Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D4812 |
Note Message | |
---|---|
1 . | 50 mm/min |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Tarnamid® T- 30 MHLS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
Unigel PS U8875 | Unigel Plásticos | PS (HIPS) | Unigel PS |
ELASTOSIL® P 7616-195 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
KEBAFORM® C 1090 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
ESTOPLAST XU 425NGY144 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |