TECACOMP® PA66 TC white 3923
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0b1BBH_TECACOMPPA66TCwhite3923.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 45 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 31.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.79 | % | ISO 294-4 |
| Flow | 0.77 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ISO 527-2/50 |
| Tensile Stress | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | °C | ISO 75-2/A |
| Glass Transition Temperature | 50.0 | °C | DIN 53765 |
| Melting Temperature | 255 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 10 to 40°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 60 to 100°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 10 to 40°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 60 to 100°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1210 | J/kg/°C | DIN EN 821 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 1.5 | W/m/K | DIN EN 821 |
| -- 2 | 4.5 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C | |
| Thermal Diffusivity | DIN EN 821 | ||
| In-plane | 2.10 | cSt | DIN EN 821 |
| Through-plane | 0.800 | cSt | DIN EN 821 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 3.9E+13 | ohms·cm | DIN EN 61340 |
| Dielectric Constant | DIN 53483 | ||
| 1.00 GHz | 3.59 | DIN 53483 | |
| 2.00 GHz | 3.50 | DIN 53483 | |
| Dissipation Factor | DIN 53483 | ||
| 1.00 GHz | 6.1E-3 | DIN 53483 | |
| 2.00 GHz | 9.2E-3 | DIN 53483 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Processing (Melt) Temp | 260 - 295 | °C | |
| Mold Temperature | 100 - 150 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYVIN® PVC 6820 | A. Schulman Inc. | PVC, Unspecified | POLYVIN® |
| Unichem 8311A | Colorite Polymers | PVC, Unspecified | Unichem |
| Dorlyl PVC GFF 64D | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |
| Sylvin 83000-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| OTECH PVC OW752 - Riser Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |