CERTENE™ LLBF-122F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0aKGof_CERTENE-LLBF-122F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LLBF-122F is a certified prime resin Butene-comonomer, specially designed for production of high performance Blown films for general purpose packaging. LLBF-122F features excellent combination of easy processability with very good film strength as well as wide heat sealing temperature range. LLBF-122F major applications include garment bags, produce bags and liners. Maximum recommended film drawdown is 0.5 mil. LLBF-122F contains high slip and high antiblock. LLBF-122F complies with FDA regulation 21CFR 177.1520 (c) 3.1 (a) and with most international regulations concerning the use of Polyethylene in conct with food articles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 214 | MPa | ASTM D882 |
| 1% secant, TD | 248 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.0 | MPa | ASTM D882 |
| TD : Yield | 11.0 | MPa | ASTM D882 |
| MD : Fracture | 44.8 | MPa | ASTM D882 |
| TD : Fracture | 29.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 650 | % | ASTM D882 |
| TD : Fracture | 990 | % | ASTM D882 |
| Dart Drop Impact 1 | 85 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 80 | g | ASTM D1922 |
| TD | 550 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 121 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 65 | ASTM D2457 | |
| Haze | 7.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Specimen: 1.0 mils (25 µm) film, melt temperature 395-430°F (200-220°C), blow-up-ratio 2.5 :1. |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0219 | Borealis AG | Plastomer | Queo™ |
| VESTAMID® HTplus M3033 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| Badadur® PBT8 GF30 TM-Z2 | Bada AG | PBT | Badadur® |
| Complet® LCF40-TPU | PlastiComp, Inc. | ETPU | Complet® |
| ESTYRENICS 352 | PCC Plastics & Consultations Center | PS (GPPS) | ESTYRENICS |