Edgetek™ QT020GFS/000 FR NATURAL - "OBSOLETE"
| Category: | SPS , Syndiotactic Polystyrene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0ZGGgx_Edgetek-QT020GFS-000-FR-NATURAL---OBSOLETE-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Edgetek™ QT020GFS/000 FR NATURAL - "OBSOLETE" is a Syndiotactic Polystyrene (SPS) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 9000 | MPa | ISO 527 |
| Tensile Strength 2(Break) | 120 | MPa | ISO 527 |
| Tensile Elongation 3(Break) | 1.3 | % | ISO 527 |
| Flexural Modulus | 9500 | MPa | ISO 178 |
| Flexural Strength | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 34 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 230 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 270 to 320 | °C | |
| Mold Temperature | 80.0 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1511AH | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Sylvin 6411-92 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ESTAPROP KUR 1010 TG05 | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Karina CLEAR PVC COMPOUND 70/213-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax CA 1110 G4 LS 1740 | LyondellBasell Industries | PP Copolymer | Hifax |