Baydur® 661 IBS (30 pcf, 20% Wollastocup) Datasheet,PUR-MDI,Covestro

Message
Baydur 661 IBS is a gray-pigmented, rigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a polymeric diphenylmethane diisocyanate (PMDI), and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives. Note: Component B should be agitated thoroughly prior to delivery of drum contents to day tank due to possible pigment settling. The Baydur 661 IBS system is used in transportation, industrial, and recreational markets. The applications typically take advantage of the material's strength, excellent surface finish, and large-part capability. As with any product, use of the Baydur 661 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.

General Information
Features	Good strength Excellent appearance
Uses	Structural Foam Industrial application
Appearance	Grey
Processing Method	Reaction Injection Molding (RIM)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.479	g/cm³	ASTM D792

Hardness	Nominal Value	Test Method
Durometer Hardness		ASTM D2240
Shaw D, 6.35mm	54	ASTM D2240
Shaw D, 12.7mm	60	ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Fracture, 6.35mm	9.65	MPa	ASTM D638
Fracture, 12.7mm	11.0	MPa	ASTM D638
Tensile Elongation			ASTM D638
Fracture, 6.35mm	5.0	%	ASTM D638
Fracture, 12.7mm	5.0	%	ASTM D638
Flexural Modulus			ASTM D790
6.35 mm	1170	MPa	ASTM D790
12.7 mm	793	MPa	ASTM D790
Flexural Strength			ASTM D790
6.35 mm	23.4	MPa	ASTM D790
12.7 mm	20.7	MPa	ASTM D790
Compressive Strength			ASTM D695
6.35 mm	19.3	MPa	ASTM D695
12.7 mm	13.8	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength			Internal method
-- ¹	4.6	kJ/m²	Internal method
-- ²	5.0	kJ/m²	Internal method

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, unannealed, 6.35mm	80.0	°C	ASTM D648
0.45 MPa, unannealed, 12.7mm	85.0	°C	ASTM D648

Thermoset	Nominal Value
Thermoset Components
Component a	Mixing ratio by weight: 120
Component B	Mixing ratio by weight: 100

Additional Information
Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Flash Point PMCC: 199°C NCO: 31.5 wt% Part B Type: Polyol Appearance: Medium gray liquid Specific Gravity @ 25°C: 1.11 Viscosity @25°C: 1800 cps Flash Point PMCC: 117°C Water: 0.35 wt% Material Temperatures: 32 to 35°CMold Temperature: 55 to 66°CHand Mix Reactivity at 25°C Cream Time: 16 to 26 sec Gel Time: 30 to 40 sec Tack Free Time: 50 to 60 sec Free-Rise Density: 13 to 15 lb/ft³ Polyol Nucleation Specific Gravity: 0.85 to 0.95 0Recommended Shot Time: 5 to 6 secTypical cure Time, 0.500 in Thickness: 5 sec

Additional Information

Part A Type: Isocyanate Appearance: Dark brown liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Flash Point PMCC: 199°C NCO: 31.5 wt% Part B Type: Polyol Appearance: Medium gray liquid Specific Gravity @ 25°C: 1.11 Viscosity @25°C: 1800 cps Flash Point PMCC: 117°C Water: 0.35 wt% Material Temperatures: 32 to 35°CMold Temperature: 55 to 66°CHand Mix Reactivity at 25°C Cream Time: 16 to 26 sec Gel Time: 30 to 40 sec Tack Free Time: 50 to 60 sec Free-Rise Density: 13 to 15 lb/ft³ Polyol Nucleation Specific Gravity: 0.85 to 0.95 0Recommended Shot Time: 5 to 6 secTypical cure Time, 0.500 in Thickness: 5 sec

Note Message
1 .	0.5
2 .	0.25 in

Category:	PUR-MDI , Polyurethane (MDI)
Manufacturer:	Covestro - PUR
Trademark:	Baydur®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0YTywz_Baydur-661-IBS-30-pcf-20-Wollastocup-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RoyalEdge® 5030	Lion Copolymer, LLC	EPDM	RoyalEdge®
Starex WR-9100	SAMSUNG SDI CO., LTD.	ASA	Starex
TOTAL Polypropylene PPH 3825WZ	TOTAL Refining & Chemicals	PP Homopolymer	TOTAL Polypropylene
Huafon JF-S-AH7090	Huafon Group Co., Ltd.	PUR, Unspecified	Huafon
Osterlene® LLDB-2-919	Osterman & Company	LLDPE	Osterlene®