INEOS LLDPE LL6910AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0XUM9I_INEOS-LLDPE-LL6910AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL6910AA is particularly suitable for use in lean and rich blend blown film applications, such as overwrap, counter bags, shrink film (lean blends, 10 to 30% LLDPE) and boil-in-the-bag applications. This grade is also recommended for artificial grass applications. LL6910AA is a linear low density polyethylene copolymer containing hexene-1 as the comonomer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS O&P Europe technical representative for further advice on the use of LL6910AA. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.936 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus - 1% Secant (38 µm, Blown Film) | 450 | MPa | ISO 1184 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, blown film | 18.0 | MPa | ISO 527-3 |
| TD : Yield, 38 µm, blown film | 21.0 | MPa | ISO 527-3 |
| MD : 38 µm, blown film | 54.0 | MPa | ISO 527-3 |
| TD : 38 µm, blown film | 36.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 1184 | ||
| MD : Broken, 38 µm, blown film | 780 | % | ISO 1184 |
| TD : Broken, 38 µm, blown film | 990 | % | ISO 1184 |
| Dart Drop Impact (38 µm, Blown Film) | 65 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 38.0 µm | 13.7 | kN/m | ASTM D1922 |
| TD : 38.0 µm | 127.5 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 38 µm film, 2:1 blow up ratio, 230°C melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 612 GF 30 HI | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| TECHNYL® 1015CR BRIGHT | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Vydyne® 22HSP BK | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| OTECH PVC PF5513-Sandal | OTECH Corporation | PVC, Unspecified | OTECH PVC |
| ULTEM™ 1100F resin | SABIC Innovative Plastics | PEI | ULTEM™ |