SURPASS® RMs245-U(UG)

Category:	HDPE , High Density Polyethylene
Manufacturer:	NOVA Chemicals
Trademark:	SURPASS®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0Wyfkm_SURPASSRMs245UUG.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

SURPASS®RMs245-U(UG) is a high density polyethylene material,. This product is available in North America and is processed by rotational molding.

SURPASS®The main features of RMs245-U(UG) are:

flame retardant/rated flame

High stiffness

High resistance to environmental stress fracture (ESCR)

Antioxidants

beautiful

Typical application areas include:

food contact applications

Water pipes/pipes/drinking water

Jars

Agriculture

General Information
Additive	Antioxidation UV stabilizer
Features	UV Stabilized Rigidity, high High ESCR (Stress Cracking Resistance) Resistance to gas fading Antioxidation Low temperature impact resistance Good appearance Octene comonomer
Uses	Agricultural application Water tank
Agency Ratings	FDA 21 CFR 176.170(c), Table 1 FDA 21 CFR 176.170(c), Table 2, Cond. B FDA 21 CFR 176.170(c), Table 2, Cond. C FDA 21 CFR 176.170(c), Table 2, Cond. D FDA 21 CFR 176.170(c), Table 2, Cond. E FDA 21 CFR 176.170(c), Table 2, Cond. F FDA 21 CFR 176.170(c), Table 2, Cond. G FDA 21 CFR 176.170(c), Table 2, Cond. H FDA 21 CFR 177.1520(c) 3.2a NSF 14 NSF 61 NSF STD-24
Processing Method	rotomolding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.945	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.7	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance
50°C, 100% Igepal, compression molding, F50	> 1000	hr	ASTM D1693A
50°C, 100% Igepal, compression molding, F50	> 1000	hr	ASTM D1693B

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, 1.90 mm, Compression Molded)	23.0	MPa	ASTM D638
Tensile Elongation ²(Yield, 1.90 mm, Compression Molded)	11	%	ASTM D638
Flexural Modulus - 1% Secant (Compression Molded)	1030	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Low temperature impact- Rotational Molded			ARM
-40°C, 3.17 mm	75.0	J	ARM
-40°C, 6.35 mm	> 245	J	ARM

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	63.0	°C	ASTM D648
1.8 MPa, not annealed	43.0	°C	ASTM D648
Melting Temperature	127	°C	DSC

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Note Message
1 .	Type 4, 51mm/min
2 .	Type 4, 51mm/min

Resin Grade	Manufacturer	Category	Trademark
Sasol Polymers PE HF120	Sasol Polymers	LLDPE	Sasol Polymers PE
Spartech Polycom PP5415	Spartech Polycom	PP, Unspecified	Spartech
Aurora PVC AP4000 Series AAMA	Aurora Plastics, Inc.	PVC, Rigid	Aurora PVC
LNP™ LUBRICOMP™ WCL36 compound	SABIC Innovative Plastics	PBT	LNP™ LUBRICOMP™
Plenco 04504 (Compression)	Plastics Engineering Co.	Phenolic	Plenco