HiPrene® MT63IV
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0W5poU_HiPrene-MT63IV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® MT63IV is a 16% mineral filled, impact modified polypropylene compound for Interior applications with excellent impact/stiffness balance, good flowability and good scratch resistance. It has beed primarily designed for esthetical interior parts like a dashboard and door trims. This grade is available in natural or color-matched, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.85 | % | Internal method |
| Flow direction | 0.85 | % | Internal method |
| Ash Content (600°C) | 16 | % | ISO 3451 |
| Volatile Matter | 0.10 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Anti-scratch- Delta L 1 | 1.10 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 70 | mm/min | TL 1010 |
| Fogging 2(100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | g | VDA 277 | |
| Odor 3(80°C) | 2.60 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 21.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus 4(23°C) | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 4.00 - 6.50 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumInjection Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | Performed on black plaques with rough structure, acc. PV 3952 |
| 2 . | 16 hr |
| 3 . | 2 hr, acc. PV 3900 |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| mPact™ D143 | Chevron Phillips Chemical Company LLC | mLLDPE | mPact™ |
| Alkathene® XDS34 | Qenos Pty Ltd | LDPE | Alkathene® |
| AMTOPP BFP35 | Inteplast Group | PP, Unspecified | AMTOPP |
| Hostacom TRC 787N E C11323 | LyondellBasell Industries | PP Copolymer | Hostacom |
| TECACOMP® PA46 TF30 natural 3148 | Ensinger GmbH | Nylon 46 | TECACOMP® |