LNP™ THERMOCOMP™ EX11413 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0UdpZU_LNP-THERMOCOMP-EX11413-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* EX11413 is a compound based on Polyetherimide resin containing Carbon Fiber. Also known as: LNP* THERMOCOMP* Compound EX11413 Product reorder name: EX11413 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr, 50% RH) | 0.24 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11200 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 197 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 9660 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 268 | MPa | ASTM D790 |
| Poisson's Ratio | 0.44 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 520 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 213 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 380 - 400 | °C | |
| Middle Temperature | 380 - 400 | °C | |
| Front Temperature | 380 - 400 | °C | |
| Processing (Melt) Temp | 380 - 400 | °C | |
| Mold Temperature | 165 - 180 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 50 - 100 | rpm |
| Injection instructions |
|---|
| Injection Speed: 40 - 70 mm/s |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300.5 C | RTP Company | PPS | RTP |
| SLOVAMID® 66 W 30 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| TOTAL Polypropylene PPH 9040 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Blendfor® A 4000 NATURALE | SO.F.TER. SPA | PC+ABS | Blendfor® |
| Geon™ Vinyl Flexible A75M1 Trans 9000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |