InnoPlus LL7410A
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0TibGw_InnoPlus-LL7410A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus LL7410A resin is a linear low density polyethylene with butene comonomers, without slip and antiblock. This grade offers the excellent machinability on conversion lines. Film extruded from InnoPlus LL7410A have high tensile strength, elongation, good toughness and outstanding puncture strength. It is available for tubular blown film processing. Besides, this grade can be used for blending with HDPE as well. InnoPlus LL7410A is recommended for producing the general purpose films, liners, heavy duty films, food packaging and agricultural films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 52 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 11.0 | MPa | |
| Break, Compression Molded | 28.0 | MPa | |
| Tensile Elongation (Break, Compression Molded) | 790 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 310 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 190 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 220 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 34.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 26.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 700 | % | |
| TD : Break, 25 µm, Blown Film | 900 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 100 | g | |
| TD : 25 µm, Blown Film | 350 | g |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 121 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 180 | °C | |
| Die Temperature | 170 to 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1700 FR | RTP Company | PPE+PS | RTP |
| Tarnoform® 500 HI2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| NOVALAC RX®853G | Vyncolit N.V. | Phenolic | NOVALAC |
| Cellidor CP 300-20 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| Colorite 12 Series 9612 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |