Generic PC - Stainless Steel Fiber
| Category: | PC , Polycarbonate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0TcoQ7_Generic-PC---Stainless-Steel-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PC - Stainless Steel Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 - 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.20 - 0.67 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 - 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2410 - 9150 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 51.7 - 75.0 | MPa | ASTM D638 |
| 23°C | 58.4 - 97.5 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 2.0 - 10 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 10 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2380 - 5920 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 62.1 - 146 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 47 - 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 410 - 1400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 137 - 152 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 126 - 141 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 25 - 2.5E+8 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 0.0 - 2.5E+8 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 122 | °C | |
| Drying Time | 3.0 - 4.1 | hr | |
| Suggested Max Moisture | 0.020 - 0.10 | % | |
| Rear Temperature | 279 - 316 | °C | |
| Middle Temperature | 279 - 324 | °C | |
| Front Temperature | 279 - 327 | °C | |
| Processing (Melt) Temp | 291 - 316 | °C | |
| Mold Temperature | 79.4 - 96.1 | °C | |
| Injection Pressure | 85.9 - 121 | MPa | |
| Back Pressure | 0.258 - 0.349 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PC - Stainless Steel FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND R3 | POLY GIN | PC | MARCOBLEND |
| Tarnamid® T- 27 GF20 FRV0 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| ELASTOSIL® P 7616-160 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| Kazan LLDPE PE2NT06-6 | Kazanorgsintez Joint Stock Company | LLDPE | Kazan LLDPE |
| SD POLYCA™ IM6120 | Sumika Styron Polycarbonate Limited | PC+ABS | SD POLYCA™ |