RTP 200 FR NH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0TOeqh_RTP-200-FR-NH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced - Flame Retardant - Halogen Free |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.4 - 1.8 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.95 | % | ASTM D570 |
| Moisture Content | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4140 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 3790 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 960 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 188 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm, ** Values per RTP Company testing.) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (3.00 mm) | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 254 - 277 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® ET2613 | Covestro - Polycarbonates | PC | Makrolon® |
| Tekumid 6 SC/GK 30 | TEKUMA Kunststoff GmbH | Nylon 6 | Tekumid |
| Pearlthane® ECO D12T90E | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlthane® ECO |
| PETILEN YY F 00556 (HMW) | PETKIM Petrokimya Holding A.S. | HDPE | PETILEN |
| KOCETAL® CF302 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |