Plaslube® PPS GF30 SL2
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Plaslube® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0SsYYQ_Plaslube-PPS-GF30-SL2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plaslube® PPS GF30 SL2 is a Polyphenylene Sulfide (PPS) product filled with glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.35 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 107 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 10700 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.16 | ||
| vs. Steel - Static | 0.14 | ||
| Wear Factor | 160 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 266 | °C | |
| 1.8 MPa, Unannealed | 260 | °C | |
| CLTE - Flow | 1.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 22 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 163 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 288 to 304 | °C | |
| Middle Temperature | 316 to 343 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 316 to 332 | °C | |
| Processing (Melt) Temp | 324 to 338 | °C | |
| Mold Temperature | 129 to 163 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE CP 191XP | Braskem | PP Copolymer | Braskem PE |
| DENKA EVA TEX 80 | Denka Company Limited | EVA | DENKA EVA TEX |
| Fainplast PVC PG 7030 | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| Ebalta Silicone High Solid | Ebalta Kunststoff GmbH | Silicone | Ebalta |
| Sylvin 4299-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |