LOFEX® A311A
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0SgrXB_LOFEX-A311A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A311A is Polyester film is optically clear and inside corona / outside acryl treated with enhanced adhesion to inks and coatings. So, it can use by window film, label and print film. Also, it has excellent properties by tensile strength, proper elongation and the thermal contraction rate. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.30 | ||
| vs. Itself - Static | 0.35 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 196 | MPa | |
| MD : Yield, 100 µm | 196 | MPa | |
| TD : Yield, 50 µm | 235 | MPa | |
| TD : Yield, 100 µm | 235 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 160 | % | |
| MD : Break, 100 µm | 170 | % | |
| TD : Break, 50 µm | 110 | % | |
| TD : Break, 100 µm | 120 | % | |
| F5 | ASTM D882 | ||
| MD : 50.0 µm | 113 | MPa | |
| MD : 100.0 µm | 113 | MPa | |
| TD : 50.0 µm | 113 | MPa | |
| TD : 100.0 µm | 113 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 150°C, 50.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 50.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| Surface Treatment | Inside (Corona)/Outside (Acryl) |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60°, 50.0 µm | 170 | ||
| 60°, 100 µm | 170 | ||
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 89.0 | % | |
| 100 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 50.0 µm | 1.3 | % | |
| 100 µm | 2.1 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M6113 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sinvicomp SIM4009 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| DURANEX® 733LD | Polyplastics Co., Ltd. | PBT+SAN | DURANEX® |
| Koylene ADL AM120N | Reliance Industries Limited | PP Homopolymer | Koylene ADL |
| K-Bin Rigid PVC KB-5026 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |