TEKASTER™ F615G55
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKASTER™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0RuptT_TEKASTER-F615G55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| F615G55 is GF 55% reinforced polyethylene terephthalate (PET). F615G55 has good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 188 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 17900 | MPa | ASTM D790 |
| Flexural Strength 4 | 289 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 246 | °C | |
| 1.8 MPa, Unannealed | 229 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 245 to 255 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 255 to 265 | °C | |
| Nozzle Temperature | 255 to 265 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 G40 MI | NUREL, S.A. | Nylon 6 | Promyde® |
| VITAMIDE® AL38BK9009 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| OnForce™ LFT LF0100-5002 NATURAL | PolyOne Corporation | PUR, Unspecified | OnForce™ LFT |
| Sumiliteresin® PR-1052 I | SBHPP | Phenolic | Sumiliteresin® |
| Romiloy® 4010 GF30 | ROMIRA GmbH | ABS+Nylon | Romiloy® |