Amilan® CM3004G-30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0RntKK_Amilan-CM3004G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM3004G-30 is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.59 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.60 to 0.90 | -- | % | |
| Flow : 3.00 mm 2 | 0.20 to 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.60 | -- | % | |
| Saturation, 23°C | 4.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 121 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 190 | -- | MPa | |
| 23°C | 165 | 135 | MPa | |
| 80°C | 110 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 2.5 | -- | % | |
| Break, 23°C | 3.0 | 3.0 | % | |
| Break, 80°C | 4.5 | -- | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 10200 | -- | MPa | |
| 23°C | 9300 | 6500 | MPa | |
| 80°C | 5500 | -- | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 275 | -- | MPa | |
| 23°C | 250 | 200 | MPa | |
| 80°C | 150 | -- | MPa | |
| Taber Abrasion Resistance (1000 Cycles) | 26.0 | -- | mg | ISO 9352 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 7.0 | -- | kJ/m² | |
| 23°C | 9.5 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 65 | 70 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 251 | -- | °C | ISO 75-2/B |
| Melting Temperature | 265 | -- | °C | DSC |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 38 | 33 | kV/mm | IEC 60243-1 |
| Dielectric Constant 3 | IEC 60250 | |||
| 23°C, 1 kHz | 4.00 | -- | ||
| 23°C, 1 MHz | 0.0100 | -- | ||
| Arc Resistance 4 | 70.0 | -- | sec | UL 746 |
| Comparative Tracking Index (CTI) | 200 | -- | V | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.397 mm) | V-0 | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | 60% RH |
| 4 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D UV | RTP Company | Nylon 612 | RTP |
| Stat-Rite® SIS-534 | Lubrizol Advanced Materials, Inc. | PS (HIPS) | Stat-Rite® |
| Stylac™ 121 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Sylvin 8220-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 7868-70C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |