REPOL® H230FG
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Qz59E_REPOL-H230FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol H230FG is recommended for use in Fibre Spinning and in particular bulk continuous filaments. Repol H230FG contains an excellent process stabilizer package suitable for filament products. Formulated for gas fading resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 34.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 10 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1550 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-8162 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| TULAMID® PA-SV15-LT1 | UCC Shchekinoazot | Nylon 6 | TULAMID® |
| Zythane® 6045D | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| Hostaform® C 9021 FCT1 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Zytel® FR7026V0F NC010 | DuPont Performance Polymers | Nylon 66 | Zytel® |