| Hostacom X M3 T08 is 25% mineral filled copolymer. The grade features very high rigidity with good impact resistance. Typical customer applications are autmotive intrument panel. The grade is UV-stabilized for interior automotive applications. Grade is available in custom colour, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 11.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 55.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 2200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 20.0 | MPa | |
| Break | 15.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 2.7 | % | |
| Break | 22 | % | |
| Flexural Modulus - Secant | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.7 | kJ/m² | |
| 0°C, Complete Break | 6.0 | kJ/m² | |
| 23°C, Complete Break | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 46 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1000 TFE 20 FR A | RTP Company | PBT | RTP |
| 4PROP® 9C23200 | 4Plas | PP Copolymer | 4PROP® |
| Laprene® 83FM00A65 | SO.F.TER. SPA | SEBS | Laprene® |
| OLEFISTA™ QX0238D | Mitsubishi Chemical Performance Polymers, Inc. | Elastomer, Specialty | OLEFISTA™ |
| 3M™ Dyneon™ Fluoroelastomer FE 5830Z | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |