Hylex® P1317 L1 HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Pbnn6_Hylex-P1317-L1-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, UV Stabilized, Higher Flow, Mold Release, Water Clear |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 68.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength | 95.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 129 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | 88.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 10 Z1 G4 | Taro Plast S.p.A. | PBT | TAROLOX |
| BR® 4535A | Cytec Industries Inc. | Epoxy | BR® |
| Halar® 930LC | Solvay Specialty Polymers | ECTFE | Halar® |
| ENGAGE™ 8157 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |
| Karina IVORY PVC COMPOUND 751-35/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |