Ketron® PEEK (CM)
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Ketron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0OwMr3_Ketron-PEEK-CM-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ketron PEEK grades offer chemical and hydrolysis resistance similar to PPS, but can operate at higher temperatures. Unreinforced, compression molded Ketron PEEK offers good wear resistance. It can be used continuously to 480°F (250°C) and in hot water or steam without permanent loss in physical properties. For hostile environments, PEEK is a high strength alternative to fluoropolymers. PEEK carries a V-O flammability rating and exhibits very low smoke and toxic gas emission when exposed to flame. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | |
| Saturation | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 90 | ||
| R-Scale | 125 | ||
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 4140 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 172 | MPa | ASTM D790 |
| Compressive Modulus | 3100 | MPa | ASTM D695 |
| Compressive Strength | 117 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.40 | Internal Method | |
| Wear Factor | 710 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 249 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.438 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 340 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM F433 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | > 1.0E+13 | ohms | Internal Method |
| Dielectric Strength 4 | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 3.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203 TE 18 SI 2 | RTP Company | Nylon 66 | RTP |
| RheTech Polypropylene CC20P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| TAROPRENE® 1 A55 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| NYLOY® MS-0100N | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |
| LNP™ THERMOCOMP™ RF0049SP compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |