KOPLA PA66 KDG1060
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0NkFV2_KOPLA-PA66-KDG1060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA66 KDG1060 is a Polyamide 66 (Nylon 66) material filled with glass fiber. It is available in Asia Pacific. Primary attribute of KOPLA PA66 KDG1060: Flame Rated. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 127 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4900 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 250 | °C | |
| 1.8 MPa, Unannealed | 240 | °C | |
| Melting Temperature | 260 | °C | |
| CLTE - Flow | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon F2538H-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| Tarnoform® 300 EC1 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Bapolene® LL200F | Bamberger Polymers, Inc. | LLDPE | Bapolene® |
| Futerro® Fiber Melt Spinning | Futerro | PLA | Futerro® |
| Pearlthane® MB-51UV | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® |