BJB Polyurethane TC-850 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0NWeSz_BJB-Polyurethane-TC-850-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TC-850 A/B produces a high impact rigid 75 Shore D material that is commonly used to make computer housings, models of all kinds, artwork, and can also be used for electronic component encapsulation. It provides a working time of 6 - 7 minutes. PRODUCT HIGHLIGHTS:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.06 | g/cm³ | |
| -- 2 | 1.10 | g/cm³ | |
| -- | 1.12 | g/cm³ | ASTM D792 |
| Specific Volume | 0.925 | cm³/g | |
| Shrinkage 3 | 0.60 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 7.0 - 8.0 | min | |
| Work Time 4(25°C) | 6.0 - 7.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 - 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 46.9 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus | 1670 | MPa | ASTM D790 |
| Flexural Strength | 67.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 95.0 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 89.4 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 50, mixing ratio by capacity: 52 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 5 | 160 | cP | ASTM D2393 |
| 25°C 6 | 1350 | cP | ASTM D2393 |
| 25°C 7 | 75.0 | cP | ASTM D2393 |
| Demold Time (25°C) | 60 - 120 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Note: Reported physical properties based on elevated temperature cured test specimens.In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 180°F (82°C). Support of the part may be required to prevent part deformation during heat cure. |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 12" x 1/2" x 1/2" |
| 4 . | 100g mass |
| 5 . | Mixed |
| 6 . | Part B |
| 7 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2914-80 White 125 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| THERMOLAST® K TC8FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Nipol® NX775 | Zeon Chemicals L.P. | NBR | Nipol® |
| Hostacom EKC 330N E1 D62813 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Hifax TYC 762P | LyondellBasell Industries | TPO (POE) | Hifax |