Starex SR-0315 V
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0MUrPg_Starex-SR-0315-V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex SR-0315 V is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 26 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 109 | ASTM D785 | |
| R-Scale | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 39.0 | MPa | ASTM D638 |
| Yield | 42.0 | MPa | ISO 527-2/50 |
| Break 3 | 32.0 | MPa | ASTM D638 |
| Break | 33.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 41 | % | ASTM D638 |
| Break | 32 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2200 | MPa | ASTM D790 |
| -- 6 | 2500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 63.0 | MPa | ASTM D790 |
| -- 8 | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 250 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 210 | J/m | ASTM D256 |
| 23°C 10 | 24 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 99.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 100 | °C | ISO 306/B50 |
| -- | 102 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® ASA30U | A. Schulman Europe | ASA | RONFALIN® |
| Victron® 095C2-WR | Asia International Enterprise (Hong Kong) Limited | PEEK | Victron® |
| Arnite® AV2 340 XL | DSM Engineering Plastics | PBT | Arnite® |
| LEXAN™ CFR7431 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| ULTEM™ 2210R resin | SABIC Innovative Plastics | PEI | ULTEM™ |