NatureFlex™ 90 D-NE
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | NatureFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0M3TmT_NatureFlex-90-D-NE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NatureFlex™ 90 D-NE is a Regenerated Cellulose product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of NatureFlex™ 90 D-NE include coating applications and film. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 1(vs. Itself - Dynamic) | 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 22 µm | > 3000 | MPa | |
| 1% Secant, TD : 22 µm | > 1520 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 22 µm | 124 | MPa | |
| TD : Yield, 22 µm | 68.9 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 22 µm | 22 | % | |
| TD : Break, 22 µm | 70 | % | |
| Seal Strength 2 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature (22 µm) | 79.4 to 199 | °C | Internal Method |
| Oxygen Transmission Rate (Wet) (24°C, 22 µm, 0.0% RH) | 2.95 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission 3 | 50 | g/m²/24 hr | ASTM E96 |
| Film Gauge | 22.1 | µm | Internal Method |
| Yield (22.1 µm) | 31.3 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 22.1 µm) | 90 | ASTM D2457 | |
| Haze 4(22.1 µm) | 6.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Thickness: 0.87 mil |
| 2 . | Thickness: 0.87 mil |
| 3 . | 100°F, 90%RH, thickness: 0.87 mil |
| 4 . | 2.5° wide angle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC HDPE PH162 | LG Chem Ltd. | HDPE | SEETEC HDPE |
| New-prene™ 6265N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| NuSil R21-2615 | NuSil Technology | Silicone | NuSil |
| IROGRAN® A 88 H 4622 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| Karina IVORY COMP (SP31502) -E KAPU 6535/ 1-NT-MARFIM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |