ELEVATE™ EF529
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0LuK7o_ELEVATE-EF529.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake ELEVATE™ EF529AA is an ethylene vinyl acetate copolymer with 18.5% VA. EF529AA does not contain slip or antiblock, and is designed for blown and cast films requiring excellent optics and low heat seal initiation. High melt strength makes EF529AA an excellent choice for profile extrusions, molding, and foaming applications requiring medium VA content. Application/Uses: Flexible packaging films Peelable seals, adhesive layers Injection and blow molding Profile extrusions, tubing, wire & cable |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 2.5 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 32 µm, blown film | 42.1 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm, blown film | 50.3 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 24.8 | MPa | ASTM D882 |
| TD : Broken, 32 µm, blown film | 24.1 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 32 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 32 µm, blown film | 800 | % | ASTM D882 |
| Dart Drop Impact 4(32 µm, Blown Film) | 290 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 67.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 85.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 31.8 µm, Blown Film) | 82 | ASTM D2457 | |
| Haze (31.8 µm, Blown Film) | 3.6 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blown Film Melt Temperature | °C | ||
| Cast Film Melt Temperature | °C | ||
| Typical film property as measured on a 1.25 mil blown film sample fabricated at a 2.5:1 B.U.R. |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZM 43 G9 | Arkema | Nylon 11 | Rilsan® |
| RTP 201.3 HS | RTP Company | Nylon 66 | RTP |
| POLYNIL® T40 | Nilit Plastics | Nylon 66 | POLYNIL® |
| SILVER® SA-2124 | Guangdong Silver Age Sci & Tech. Co., Ltd | SEBS | SILVER® |
| NILFLEX® 8 K30T | Taro Plast S.p.A. | PP Copolymer | NILFLEX® |