Braskem PP CP 202XP
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0Loz3Z_Braskem-PP-CP-202XP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: CP 202XP is a high melt flow rate heterophasic copolymer designed to achieve parts with high stiffness and impact strength resistance, low warpage and excellent surface appearance. Applications: Household appliances; High stiffness parts; Compounds |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 26 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale, Injection Molded | 97 | ASTM D785 | |
| R-Scale | 97 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Injection Molded) | 32.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Yield, Injection Molded) | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| 1% Secant : Injection Molded | 1600 | MPa | ASTM D790 |
| Injection Molded | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C, Injection Molded | 20 | J/m | ASTM D256 |
| 23°C, Injection Molded | 70 | J/m | ASTM D256 |
| -20°C, Injection Molded | 2.9 | kJ/m² | ISO 180 |
| 23°C, Injection Molded | 4.6 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, Injection Molded | 126 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 126 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, Injection Molded | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 1 |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novalloy-S S1500 | PlastxWorld Inc. | PC+ABS | Novalloy-S |
| Hanwha Total PP FH44N | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Huaxia Shenzhou FKM 246V | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |
| MACOMASS TPE MM-TPE O 1431 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |
| Rotuba CAP CP800 (13% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |