PRE-ELEC® TPU 1510
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0LKvA8_PRE-ELEC-TPU-1510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® TPU 1510 is a conductive compound based on a modified polyether thermoplastic polyurethane (TPU). Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® TPU 1510 has retained the excellent mechanical properties of the base elastomer. PRE-ELEC® TPU 1510 has been developed for extrusion but it can also be injection moulded. Typical applications included extruded conveyor belts, sheets, tubing, cables and injection moulded technical parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 45 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 11.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 11.0 | MPa | ASTM D638 |
| 4.00 mm | 11.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 250 | % | ASTM D638, ISO 527-2 |
| Fracture | 250 | % | ASTM D638 |
| Fracture, 4.00mm | 250 | % | ISO 527-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | 1.0E+2 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 200°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ EPDM2066-BK09W Process | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| UNITIKA Nylon 6 A1030GFL | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| Hanwha Total PP FH44 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LUVOCOM® 80-7705 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Polifor® L6 GF/20 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |