Hanwha Total PE E153F
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0IsB6R_Hanwha-Total-PE-E153F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| E153F is a EVA (ethylene-vinylacetate copolymer) resin for crosslinked foam applications including mid-sole and in-sole of athletic shoes. This grade is designed to be processed in conventional kneading and rolling equipment for mixing and dispersing crosslinking agent and foaming agent. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, F10) | 500 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 94 | ASTM D2240 | |
| Shaw D | 39 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 19.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 750 | % | ASTM D638 |
| Apparent Bending Modulus | 53.9 | MPa | ASTM D747 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 69.0 | °C | ASTM D1525 1 |
| Melting Temperature | 95.0 | °C |
| Additional Information |
|---|
| Kneader Temperature: 95 to 105 °CFoaming Temperature: 155 °CFoaming Pressure: 150 kg/cm³Curing Time: 40 minVA Content, SAMSUNG TOTAL: 15 kg force/cm² |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP270EX | Kolon Plastics, Inc. | PBT | SPESIN® |
| XYRON™ 100Z | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| ALTECH® PA6 A 2030/320 GF30 UV | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Hostacom CR 1152 F D33086 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| LNP™ VERTON™ NV006E compound | SABIC Innovative Plastics | PC+ABS | LNP™ VERTON™ |