Promyde® B30 P2 U0
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0I9VxD_Promyde-B30-P2-U0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde B30 P2 U0 is a UL certified unfilled injection moulding Polyamide 6 flame retardant (Halogen free), heat stabilized. CHARACTERISTICS Promyde B30 P2 U0 is a polyamide 6 with high mechanical strength, heat stabilized, lubricated and nucleated for injection moulding. Its halogen free flame retardant system enhances its flame behavior to V0 - UL certified . APPLICATIONS Promyde B30 P2 U0 allows a fast and efficient mould filling, and an easy mould release, that combined with its excellent mechanical properties, and its flame retardant properties make it suitable for components specially used in electrical and electronics industries. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.18 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 145 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Vertical flow direction | 0.80 - 1.1 | -- | % | |
| Flow direction | 0.90 - 1.1 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 9.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Viscosity Number | 125 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3800 | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 85.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 3.5 | 25 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 9.0 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 3400 | 1200 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 116 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 55 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 60 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 3 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 9.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 9.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.030 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (1.50 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.50 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back Pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8474-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unichem 7772 | Colorite Polymers | PVC, Unspecified | Unichem |
| DESTRON™ DSC1701GH5 | DESCO Co., Ltd. | PPA | DESTRON™ |
| Iupital® F10-01 F10-02 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| Karina IVORY PVC COMPOUND 901-35/2-DR-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |