DOWLEX™ TG 2085B
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0HpZDc_DOWLEX-TG-2085B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ TG 2085B is a Linear Low Density Polyethylene, copolymer octene, produced in the Solution Process. This resin presents an excelent balance of optical and mechanical properties. It offers downgauging, increases in productivity and packing speed. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.95 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Puncture Resistance (38 µm) | 9.02 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 38 µm | 170 | MPa | ASTM D882 |
| 2% secant, TD : 38 µm | 210 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 37.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 32.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 830 | % | ASTM D882 |
| TD : Fracture, 38 µm | 990 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 360 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 38 µm | 700 | g | ASTM D1922 |
| TD : 38 µm | 920 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 37.5 µm) | 57 | ASTM D2457 | |
| Haze (37.5 µm) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 217 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.3 英寸 (60 mm)；32:1 比率 L/D 模具间隙：70 密尔 (1.8 mm) 熔体温度：423°F (217°C) 输出：46.9 Kg/h 模具直径：5.9 英寸 (150 mm) 放大比：2.5:1 螺杆速度：60 rpm 冷冻线高度：19.7 英寸 (50 cm) |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLON IR 1700 | POLYMA Kunststoff GmbH & Co. KG | PC | POLYLON |
| ALKAMIX™ MB-UV830 | Marplex Australia Pty. Ltd. | PE, Unspecified | ALKAMIX™ |
| Amilan® CM1026 | Toray Resin Company | Nylon 6 | Amilan® |
| Grilon® F 34 NL | EMS-GRIVORY | Nylon 6 | Grilon® |
| Sylvin 8663-65 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |