STYRON A-TECH™ 1180
| Category: | PS (HIPS) , Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON A-TECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0H0v0d_STYRON-A-TECH-1180.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON A-TECH™ 1180 advanced technology polystyrene resin is a high-impact resin with a unique combination of high gloss, high heat, excellent stiffness and good practical toughness. It is designed for injection molding applications. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 28.3 | MPa | |
| Yield, Injection Molded | 33.8 | MPa | |
| Ultimate, Compression Molded | 21.4 | MPa | |
| Ultimate, Injection Molded | 31.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, Compression Molded | 30 | % | |
| Break, Injection Molded | 55 | % | |
| Flexural Modulus | ASTM D790 | ||
| Compression Molded | 1800 | MPa | |
| Injection Molded | 2070 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Compression Molded | 50.3 | MPa | |
| Injection Molded | 60.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, Compression Molded | 80 | J/m | |
| 23°C, Injection Molded | 110 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed | 75.0 | °C | |
| 1.8 MPa, Annealed | 98.9 | °C | |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| CLTE - Flow | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 95 | ASTM D523 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1001 GB 20 | RTP Company | PBT | RTP |
| TEREZ PA 6.6 8750 T GF 30 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| AvaSpire® AV-742 SL30 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| KumhoSunny AES HW600FR | Shanghai KumhoSunny Plastics Co., Ltd. | AES | KumhoSunny AES |
| LNP™ THERMOCOMP™ IF006 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |