Miramid® VE15C

Category:	Nylon 6 , Polyamide 6
Manufacturer:	BASF Leuna GmbH
Trademark:	Miramid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0GelVb_Miramid-VE15C.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Miramid® VE15C is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber. It is available in Europe for injection molding.

Important attributes of Miramid® VE15C are:

Chemical Resistant

Crystalline

Fast Molding Cycle

Good Stiffness

Mold Release Agent

Typical applications include:

Automotive

Engineering/Industrial Parts

Coating Applications

Construction Applications

Electrical/Electronic Applications

General Information
Filler / Reinforcement	Glass Fiber, 15% Filler by Weight
Additive	Mold Release
Features	Crystalline Fast Molding Cycle Fuel Resistant Good Flow Good Stability Good Stiffness Grease Resistant High Rigidity Oil Resistant Solvent Resistant
Uses	Automotive Applications Building Materials Electrical/Electronic Applications Engineering Parts Machine/Mechanical Parts Protective Coverings Sporting Goods
Forms	Granules
Processing Method	Injection Molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1)

Physical	Dry	Conditioned	Unit	Test Method
Density	1230	--	kg/m³	ISO 1183 ¹
Water Absorption				ISO 62 ²
Saturation	8.5	--	%
Equilibrium	2.0	--	%
Viscosity number	145	--	cm³/g	ISO 307, 1157, 1628 ³

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	5500	3200	MPa	ISO 527-2 ⁴
Tensile Stress (Break)	125	75.0	MPa	ISO 527-2 ⁵
Tensile Strain (Break)	3.0	11	%	ISO 527-2 ⁶
Flexural Modulus	190	100	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA ⁷
-30°C	6.00	--	kJ/m²
23°C	7.00	11.0	kJ/m²
Charpy impact strength				ISO 179/1eU ⁸
-30°C	35.0	--	kJ/m²
23°C	45.0	100	kJ/m²

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load				ISO 75-2 ⁹
0.45 MPa	210	--	°C
1.8 MPa	190	--	°C
Melting Temperature (DSC)	220	--	°C	ISO 3146

Electrical	Dry	Conditioned	Unit	Test Method
Volume resistivity	1.0E+13	1.0E+10	ohms·m	IEC 60093 ¹⁰
Dielectric Constant (1 MHz)	3.50	6.00		IEC 60250
Dissipation Factor (1 MHz)	0.020	0.25		IEC 60250 ¹¹
Comparative tracking index	550	--		IEC 60112 ¹²

Injection	Dry	Unit
Processing (Melt) Temp	260 to 280	°C
Mold Temperature	80.0 to 100	°C

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
SABIC® PPcompound 3320EH	Saudi Basic Industries Corporation (SABIC)	PP, Unspecified	SABIC® PPcompound
Ultradur® B 4330 G6 HR BK15045	BASF Corporation	PBT	Ultradur®
NatureFlex™ NE White	Innovia Films Ltd.	Cellulose, Regenerated	NatureFlex™
ACRYLITE® Film 0F014	Evonik Cyro LLC	Film, PMMA	ACRYLITE® Film
Exxelor™ VA 1803	ExxonMobil Chemical	TP, Unspecified	Exxelor™