DOW™ HDPE KS 10100 UE
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 0GASX0_DOW-HDPE-KS-10100-UE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HDPE KS 10100 UE polyethylene resin is a kind of high-density polyethylene resin, which has improved processing performance. When applied to outdoor environment, it has excellent impact strength, stress cracking performance and ultraviolet stability, and can reduce warpage to the lowest level. remarks: when applied to the application field of contact food, HDPE KS 10100 UE polyethylene resin should meet the requirements of the U.S. food and drug administration regulations and the food contact regulations of most European countries without modification and the processing process follows the requirements of good manufacturing practices. Please contact your nearest Dow representative for proof of compliance with the Food Contact Act. The purchaser remains responsible for determining whether the use of its products complies with all relevant regulations. Application field:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.955 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 4.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 12 | g/10 min | ISO 1133 |
| Spiral Flow | 63.5 | cm | Internal method |
| Molding Shrinkage - Flow 1(250°C) | 2.6 | % | ASTM D955 |
| Environmental Stress-Cracking Resistance 2(50°C, 100% Antarox, Compression Molded) | 10.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Fracture, molding | 27.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | > 1600 | % | ASTM D638 |
| Flexural Modulus - 2% Secant (Compression Molded) | 850 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 85.0 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 128 | °C | ISO 306/A |
| Note Message | |
|---|---|
| 1 . | 0.5 seconds injection |
| 2 . | Gap |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL STAR™ AFX 218S V50 BLACK 31N | Solvay Engineering Plastics | Nylon 66 | TECHNYL STAR™ |
| Stanyl® TC155 | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| WPP PP PRC25TF2HF-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Plavis® G40 | Comco Nylon GmbH | PI, TP | Plavis® |
| Sylvin 9067-90 BLUE 1840 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |