Vipel® K010-TBA-23

Category:	Vinyl Ester , Vinyl Ester
Manufacturer:	AOC, L.L.C.
Trademark:	Vipel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0FpScG_VipelK010TBA23.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
AOC's Vipel K010-TB series are promoted bisphenol A, epoxy-based vinyl ester resins dissolved in styrene and methyl methacrylate. Flame and smoke resistance is obtained by incorporating at least 60 parts of alumina trihydrate per 100 parts of resin. Vipel K010-TB series are ideally suited for use in hand lay-up, spray-up and filament winding processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required. BENEFITS Wide formulating capabilities allow for use in many processes and for optimization of cost/performance. Unique composition produces a tough and versatile resin with excellent crack and craze resistance in molded parts. Vipel K010-TB series is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat. Vipel K010-TB series resins are highly resistant to several chemical environments.

Message

AOC's Vipel K010-TB series are promoted bisphenol A, epoxy-based vinyl ester resins dissolved in styrene and methyl methacrylate. Flame and smoke resistance is obtained by incorporating at least 60 parts of alumina trihydrate per 100 parts of resin.

Vipel K010-TB series are ideally suited for use in hand lay-up, spray-up and filament winding processes where outstanding mechanical properties and excellent resistance to chemicals and heat are required.

BENEFITS
Wide formulating capabilities allow for use in many processes and for optimization of cost/performance.

Unique composition produces a tough and versatile resin with excellent crack and craze resistance in molded parts.

Vipel K010-TB series is suitable for moldings that are subjected to particularly high static or dynamic loads. Vinyl ester resins have excellent resistance to sustained heat.

Vipel K010-TB series resins are highly resistant to several chemical environments.

General Information
Additive	Flame retardancy
Features	Cracking resistance Good cracking resistance Good corrosion resistance Good chemical resistance Heat resistance, high Good toughness Flame retardancy
Agency Ratings	FDA 21 CFR 177.2420
Forms	Liquid
Processing Method	Filament power winding Sprayable Hand coating

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3600	MPa	ASTM D638
Tensile Strength	89.6	MPa	ASTM D638
Tensile Elongation (Break)	4.0	%	ASTM D638
Flexural Modulus	3700	MPa	ASTM D790
Flexural Strength	155	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	110	°C	ASTM D648

Additional Information	Nominal Value	Unit
Gel to Peak	11.0	min
HAP Content	42	%
Peak Exotherm	180	°C
Thixotropic Index	1.50

Uncured Properties	Nominal Value	Unit
Density	1.04	g/cm³
Viscosity (Brookfield LV)	0.32	Pa·s
Gel Time	23	min

Resin Grade	Manufacturer	Category	Trademark
ASTALAC™ ABS M200	Marplex Australia Pty. Ltd.	ABS	ASTALAC™
Daplen™ ED306UBB	Borealis AG	TPO	Daplen™
Five Plus™ CPP20C	Noble Polymers	PP Copolymer	Five Plus™
HiFill® PA6/6 CM30 L	Techmer Engineered Solutions	Nylon 66	HiFill®
Durethan® AKV 35 H3.0 000000	LANXESS Asia/Pacific	Nylon 66	Durethan®