NuSil MED-4120

Category:	Rubber , Rubber
Manufacturer:	NuSil Technology
Trademark:	NuSil
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	0FZscP_NuSil-MED-4120.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications. HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus. HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts. Comments: UNCATALYZED

Message

NuSil Technology's restricted materials may be considered for use in short-term implant applications, 29 days or less, or for external applications.

HCRs can be used for extrusion of tubing and profiles (rod or ribbon), in calendared sheeting for die-cutting, or in compression or transfer molded parts such as balloons, gaskets or o-rings. HCRs are clay-like in the uncured state and when cured generally exhibit very high mechanical properties and low modulus.

HCRs with a peroxide cure system have a long history in implant applications.The cure mechanism can be vinyl specific or non vinyl specific. Non vinyl specific peroxide catalysts are more commonly used with HCRs than vinyl specific peroxide catalysts.

Comments: UNCATALYZED

General Information
Uses	Washer Pipe fittings Balloon application Profile Medical/nursing supplies
Agency Ratings	USP Class VI
Processing Method	Extrusion Resin transfer molding Profile extrusion molding Compression molding Calendering

Mechanical	Nominal Value	Unit
Tensile Strength (200% Strain)	0.689	MPa

Thermoset	Nominal Value	Unit
Post Cure Time (177°C)	2.0	hr

Additional Information	Nominal Value	Unit
Cure System	Peroxide
Plasticity: 65 mils

Uncured Properties	Nominal Value	Unit
Density	1.10	g/cm³
Curing Time (116°C)	0.083	hr

Cured Properties	Nominal Value	Unit
Shore Hardness (Shore A)	25
Tensile Strength	8.96	MPa
Tensile Elongation at Break	930	%
Tear Strength	22.8	kN/m

Resin Grade	Manufacturer	Category	Trademark
PONACOM PS 5570	Ponachem Compound GmbH	PS (HIPS)	PONACOM PS
Tenite™ Butyrate 550E4861316 Clear, Trsp	Eastman Chemical Company	CAB	Tenite™ Butyrate
WINDFORM® PS	CRP Technology s.r.l.	PS (Specialty)	WINDFORM®
Double Elephant SX-304	Suzhou Double Elephant Optical Material Co., LTD.	Acrylic (PMMA)	Double Elephant
LEXAN™ 920 resin	SABIC Innovative Plastics	PC	LEXAN™